PERMAGLOSS™

PERMAGLOSS™ Clear Roof Coating is a Clear Gloss, Elastomeric Acrylic Waterproofing Protective Roof Coating. It is a water-based, high build formula that possesses excellent waterproofing properties that beautifies, protects and extends the life of most any sloped roofing surface. Forms a thick rubber like clear shield of protection that expands and contracts with varying hot and cold temperatures, plus excellent resistance to thermal shock. Unsurpassed in technology, PERMAGLOSS™ offers superior mildew resistance, excellent adhesion, U.V. resistance and a beautiful clear gloss finish. The high-performance acrylic resin and special performance additives form a clear sealer finish or clear gloss finish on most any surface and helps to restore original color. Multiple coats will progressively increase gloss and build up film thickness for increased performance. Eliminates harmful water intrusion into and onto substrate by the sheeting off of water, thus reducing the environment for mold, mildew and fungi formation and cleansing the roof of dirt and pollution. This easy to apply clear roof coating will provide many years of durable protection and outstanding beauty and will extend the roof’s life.
PERMAGLOSS™ is an inexpensive alternative solution to roofing and re-roofing. PERMAGLOSS™ offers a 7 YEAR LIMITED MATERIAL WARRANTY.

Recommended for well-draining, SLOPED roofing surfaces only. Excellent adhesion on weathered wood, shakes, plywood, clapboard, primed metal, galvanized, aluminum, tin, copper, asbestos, asphalt, urethane, polyester, primed styrofoam, fiberglass, built-up-roofs, bonded roof gravel, rolled roofing, modified bitumen membranes, mineral surfaced roofing, concrete tiles, clay tiles, masonry tiles (flat or barrel), primed synthetic or aluminum, adobe, slate, slab, properly prepared EPDM, and various other substrates. PERMAGLOSS™ is ideal for residential, commercial and industrial applications. Check out SHINGLE SEALER™ as a popular option for shingle roofs. We also have PERMACLEAR™ Clear Roof Sealant as an excellent acrylic sealer for most roof types such as metal or copper.

SURFACE PREPARATION:
Apply only to a sound, completely dry, well prepared roof surface. Leaks must be repaired before any coating is applied. Prepare surface by thoroughly pressure washing with a water and chlorine mixture using at least 1500 P.S.I. to remove any previous coatings, dirt, grease, and other foreign materials, especially mold, mildew and algae. PERMAGLOSS™ will resist mildew growth but will not kill mildew already on the surface. Patch any holes, cracks, flashings, valleys, vents, etc., with a clear acrylic waterbased caulk or sealant.

Metal:
Clean surface of all grease, oil and foreign matter before priming. Rusted metal and uncoated metal must be primed with METAL-PRIME RED-OX™, a Red Iron Oxide Primer Sealer. Use a degreaser on galvanized or coated metals which have oils or surface treatments. Check PERMAGLOSS™ adhesion on galvanized or coated metal by applying to a small area and evaluating after 48 hours. If lack of adhesion is present after evaluating, metal must be lightly scuffed without penetrating the coated finish or galvanizing.

APPLICATION PROCEDURE:
Stir well before using. Do not thin, use product as is. Do not apply when temperatures are below 45 degrees Fahrenheit or when humidity is very high. Do not apply when coating will be subjected to rain or heavy dew before it has had enough time to dry (approx. 2 to 4 hours). Drying time will vary depending on temperature, humidity and location. Apply using brush, roller or spray. Spread coating uniformly. Spread Rate will vary depending on surface. Apply each coat between 12 to 16 mils wet film thickness. Wait at least 12 hours before applying a second coat. Two coats resulting in a minimum 16 mil total dry film thickness is required
Airless Sprayers: Use at least a 1 gallon per minute piston type airless sprayer with a maximum tip size of .025. Remove all line filters and gun filters before spraying.

CLEAN UP:
Clean up all spills, tools and overspray immediately while the coating is still wet with warm soapy water.